MITSUBISHI MATERIALS CORPORATION
BACK

CBN (SINTERED CBN)

  • MB710 and MB730 for cast iron cutting.
  • BC5030 for high-speed roughing of cast irons is now available.
  • BC5030 roughing grade in combination with the AOX body allows use of up to 16 corners and enables cost-effective, high performance machining.
CBN

SELECTION STANDARD / RECOMMENDED CUTTING CONDITIONS
FINISHING
Work Material Structure Cutting Speed (SFM) Feed
(inch/rev)
Depth of Cut
(inch)
Coolant
820 1640 2460 3280 4100
Gray Cast Iron Ferritic + Pearilitic
MB710-MB730
-.012 -.020 Dry
Pearilitic

ROUGHING
Work Material Structure Cutting Speed (SFM) Feed
(inch/rev)
Depth of Cut
(inch)
Coolant
820 1640 3280 4920 6560
Gray Cast Iron Pearilitic
BC5030
─.006 ─.118 Dry

FEATURES AND BASE
Grade Application Features Main Component Coating Layer
MB710 For General Cutting General purpose grade with well balanced wear and fracture resistance. CBN TiC Al2O3
MB730 For High Speed Cuttin
For Interrupted Cutting
Has the largest CBN content and therefore displays good thermal conductivity.
It is suitable for the high temperatures that are generated in high speed cutting.
CBN (High Content)
Co Base Alloy

BC5030
High-speed machining at large depths of cutHigh-speed interrupted machining at large depths of cut High CBN content and high thermal conductivity. The whole insert is composed of sintered CBN. This enables high speed, high efficiency machining at larger depths of cut. The coating is for recognition of spent corners. CBN AIN TiN Base

APPLICATION EXAMPLES
Tool AF5000R0404D
Insert LDCN190412R (MB730)
Machine Machining Center
Workpiece AISI-35AISI-35
Cutting Condition Cutting Speed (SFM) 3940
Depth of Cut (inch) .110
Width of Cut (inch) 2.76
Table Feed (inch/min) 120
Feed per Tooth (inch/tooth) .004
Result 10 times longer tool life and 4 times higher efficiency than ceramics.
Excellent machining with a surface finish of Ra < 64!m.